High efficiency of Pt2+ - CeO2 novel thin film catalyst as anode for proton exchange membrane fuel cells
2016
Abstract The elevated price of Pt limits the large-scale implementation of commercial proton exchange membrane fuel cells, which effectively convert chemical energy into electricity. In order to increase the cost-efficiency in proton-exchange membrane fuel cells, we have designed a family of novel anode catalysts consisting of thin films of ceria with low Pt loadings sputtered on a nanostructured carbon support. Remarkably, only such small amounts of Pt are necessary for achieving power density values comparable to the reference commercial catalysts, which results in excellent specific activities of our samples. By combining photoelectron spectroscopy and catalytic performance analysis, we …
Pbca-Type In2O3: The High-Pressure Post-Corundum phase at Room Temperature.
2014
High-pressure powder X-ray diffraction and Raman scattering measurements in cubic bixbyite-type indium oxide (c-In2O3) have been performed at room temperature. On increasing pressure c-In2O3 undergoes a transition to the Rh2O3-II structure but on decreasing pressure Rh2O3-II-type In2O3 undergoes a transition to a previously unknown phase with Pbca space group which is isostructural to Rh2O3-III. On further decrease of pressure, we observed a phase transition to the metastable corundum-type In2O3 near room conditions. Recompression of the metastable corundum-type In2O3 at room temperature leads to a transition to the Rh2O3-III phase, thus showing that the Rh2O3-III phase is the post-corundum…
Pressure-Driven Isostructural Phase Transition in InNbO4: In Situ Experimental and Theoretical Investigations
2017
[EN] The high-pressure behavior of technologically important visible-light photocatalytic semiconductor In.NbO4, adopting a monoclinic wolframite-type structure at ambient conditions, was investigated using synchrotron-based X-ray diffraction, Raman spectroscopic measurements, and first-principles calculations. The experimental results indicate the occurrence of a pressure-induced isostructural phase transition in the studied compound beyond 10.8 GPa. The large volume collapse associated with the phase transition and the coexistence of two phases observed over a wide range of pressure shows the nature of transition to be first-order. There is an increase in the oxygen anion coordination num…